CSM Rubber Sheet

HOME > Boat > Boat Rubber Sheet (Hypalon Fabric)

Hypalon

Characteristics of Boat sheet

  • Stab-resistance
  • Non-buffing
  • Air-tight
  • Developed for Rubber Boat or RIBOAT
  • Strong physical property

NH 100 CSM

Base fabric : N66 - 840D
coating : Ext : Chlorosulfonated Polyethylene (CSM)
Int : Polychloroprene (CR)

Specifications Unit Direction Standard-Test Spec
Thickness mm - KS K 0506:2006 0.9 ↑
Weight g/m2 - KS K 0514:2006 1.000 ↑
Tensile Strength N/5cm Warp KS K 0521:2006
C.R.E 3TRIP METHOD 		2.000 ↑
Weft 1.800 ↑
Resistance to Weather N/5cm Warp KS K ISO 105 B04
2007 		1.700 ↑
Weft 1.500 ↑
Tear Strength N Warp KS K 0536:2009
C.R.E TONGUE
METHOD 		80 ↑
Weft 80 ↑
Tensile Strength
in Welding Part 		N/5cm - KS K 0530:2007
C.R.E 		1.500 ↑
Abrastion Resistance Weight Loss,
mg		 - KS K 0818:2006
taber Method		 500 ↓
Colorfastness to
Weather		 Grade - KS K ISO 105 B04:
2007		 4 ↑
Temperature Cycle Appearance - Ministry of Land,
Transport and Maritime
Affairs 2004-77		 NO CHANCE
Remark  

NH 210 CSM

Base fabric : N66 - 1680D
coating : Ext : Chlorosulfonated Polyethylene (CSM)
Int : Polychloroprene (CR)

Specifications Unit Direction Standard-Test Spec
Thickness mm - KS K 0506:2006 1.1 ↑
Weight g/m2 - KS K 0514:2006 1.500 ↑
Tensile Strength N/5cm Warp KS K 0521:2006
C.R.E 3TRIP METHOD 		4.900 ↑
Weft 4.900 ↑
Resistance to Weather N/5cm Warp KS K ISO 105 B04
2007 		3.920 ↑
Weft 3.920 ↑
Tear Strength N Warp KS K 0536:2009
C.R.E TONGUE
METHOD 		392 ↑
Weft 460 ↑
Tensile Strength
in Welding Part 		N/5cm - KS K 0530:2007
C.R.E 		3.920 ↑
Abrastion Resistance Weight Loss,
mg		 - KS K 0818:2006
taber Method		 500 ↓
Colorfastness to
Weather		 Grade - KS K ISO 105 B04:
2007		 4 ↑
Temperature Cycle Appearance - Ministry of Land,
Transport and Maritime
Affairs 2004-77		 NO CHANCE
Remark standard width : 57in - 146

NH 310 CSM

Base fabric : Aramide
coating : Ext : Chlorosulfonated Polyethylene (CSM)
Int : Polychloroprene (CR)

Specifications Unit Direction Standard-Test Spec
Thickness mm - KS K 0506:2006 1.0(±10%)
Weight g/m2 - KS K 0514:2006 1,300(±10%)
Tensile Strength N/5cm Warp KS K 0521:2006
C.R.E 3TRIP METHOD 		15.000 ↑
Weft 8.000 ↑
Resistance to Weather N/5cm Warp KS K ISO 105 B04
2007 		14.000 ↑
Weft 7.000 ↑
Tear Strength N Warp KS K 0536:2009
C.R.E TONGUE
METHOD 		550 ↑
Weft 700 ↑
Tensile Strength
in Welding Part 		N/5cm - KS K 0530:2007
C.R.E 		8.000 ↑
Abrastion Resistance Weight Loss,
mg		 - KS K 0818:2006
taber Method		 500 ↓
Colorfastness to
Weather		 Grade - KS K ISO 105 B04:
2007		 4 ↑
Temperature Cycle Appearance - Ministry of Land,
Transport and Maritime
Affairs 2004-77		 NO CHANCE
Puncture Resistance N - KS K 0744:2007
C.R.E		 2.,000 ↑
Remark